ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+01 - 1.E+02 | Ω | ASTM D257 |
LNP THERMOCOMP RC00A compound is based on Nylon 6/6 resin containing 50% carbon fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+01 - 1.E+02 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 255 - 290 | °C | |
Front - Zone 3 Temperature | 260 - 270 | °C | |
Middle - Zone 2 Temperature | 255 - 265 | °C | |
Rear - Zone 1 Temperature | 250 - 260 | °C | |
Mold Temperature | 40 - 65 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 238 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 33400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 331 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 24000 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.05 - 0.15 | % | SABIC method |
Density | 1.37 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 6.3E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 254 | °C | ISO 75/Af |