LNP THERMOCOMP RF0029S compound is based on Nylon 6/6 resin containing 10% glass fiber. Added features of this grade include: Flame Retardant, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 501 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy @ peak, 23°C | 8 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 275 - 290 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 102 | MPa | ISO 527 |
| Tensile Stress, break | 102 | MPa | ISO 527 |
| Tensile Strain, yield | 2.4 | % | ISO 527 |
| Tensile Strain, break | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6370 | MPa | ISO 527 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Flexural Modulus | 5900 | MPa | ISO 178 |
| Tensile Stress, yield | 101 | MPa | ASTM D638 |
| Tensile Stress, break | 101 | MPa | ASTM D638 |
| Tensile Strain, yield | 2.5 | % | ASTM D638 |
| Tensile Strain, break | 2.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 6890 | MPa | ASTM D638 |
| Flexural Stress | 151 | MPa | ASTM D790 |
| Flexural Modulus | 5510 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.98 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.3 | % | ISO 294 |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.5 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.9 - 1.1 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 - 1.4 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 219 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 249 | °C | ISO 75/Bf |
| CTE, -40°C to 40°C, flow | 4.20E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.60E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 252 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 233 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 4.32E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.56E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |