LNP THERMOCOMP RF0049S compound is based on Nylon 6/6 resin containing 20% glass fiber. Added features of this grade include: Flame Retardant, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 678 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 275 - 290 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 136 | MPa | ASTM D638 |
| Tensile Strain, break | 3.3 | % | ASTM D638 |
| Flexural Stress | 199 | MPa | ASTM D790 |
| Flexural Modulus | 7510 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 1.2 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |