LNP THERMOCOMP RF004S compound is based on Nylon 6/6 resin containing 20% glass fiber. Added features of this grade include: Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Hot-Wire Ignition (HWI), PLC 4 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 516 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 7 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 121 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 121 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 7930 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 187 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 188 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5340 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 121 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 121 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7180 | MPa | ISO 527 |
| Flexural Stress | 186 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5860 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.3 | - | ASTM D792 |
| Density | 1.3 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.5 - 0.8 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 1.6 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 255 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 236 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 3.E-06 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 8.E-06 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 253 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 226 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 115 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.