LNP THERMOCOMP RF0057E compound is based on Nylon 6/6 resin containing 25% glass fiber. Added features of this grade include: Non-Brominated & Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+12 | Ω.cm | ASTM D257 |
| Dielectric Strength, in air, 1.6 mm | 16 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.4 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.4 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Yellow Card Link 2 | View | - | - |
| UL Yellow Card Link 3 | View | - | - |
| UL Yellow Card Link 4 | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥0.9 | mm | UL 94 |
| UL Recognized, 94-5VB Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.4 | mm | UL 94 |
| UV-light, water exposure/immersion | F1 | - | UL 746C |
| Glow Wire Ignitability Temperature, 3.0 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 2.0 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.6 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.5 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 0.9 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 0.8 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 0.4 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.6 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 0.9 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 0.8 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 0.4 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 255 - 265 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 190 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.15 - 0.4 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 1.2 | % | ISO 294 |
| Water Absorption, (23°C/24hrs) | 2.64 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Ball Pressure Test, approximate maximum | 240 | °C | IEC 60695-10-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 240 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 140 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |