LNP™ THERMOCOMP™ Compound RF0057EI

LNP THERMOCOMP RF0057EI compound is based on Nylon 6/6 resin containing 25% glass fiber. Added features of this grade include: Non-brominated & Non-Chlorinated Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added
Non Cl/Br flame retardant

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Recreational/Specialty Vehicles

Applications

Possible usage of material

Automotive
Mobile Phone
Electrical
Personal Computing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Comparative Tracking Index (UL) {PLC}	0	PLC Code	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	90	J/m	ASTM D256
Izod Impact, unnotched, 23°C	820	J/m	ASTM D4812
*Izod Impact, notched 80103 +23°C*	9.6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	51	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	85	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.4 - 0.8	%
Melt Temperature	260 - 280	°C
Nozzle Temperature	260 - 280	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	260 - 270	°C
Rear - Zone 1 Temperature	250 - 270	°C
Mold Temperature	60 - 100	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	121	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	3.3	%	ASTM D638
Tensile Modulus, 50 mm/min	10200	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	8100	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	190	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	123	MPa	ISO 527
Tensile Strain, break, 50 mm/min	3.1	%	ISO 527
Tensile Modulus, 1 mm/min	10250	MPa	ISO 527
Flexural Strength, 2 mm/min	193	MPa	ISO 178
Flexural Modulus, 2 mm/min	8280	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.43	-	ASTM D792
Melt Flow Rate, 270°C/1.2 kgf	4.8	g/10 min	ASTM D1238
Water Absorption, (23°C/24hrs)	0.55	%	ISO 62-1
Mold Shrinkage, flow	0.15 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.9 - 1.2	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	254	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	232	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	230	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES