LNP™ THERMOCOMP™ Compound RX12402

LNP THERMOCOMP RX12402 compound is based on Nylon 6/6 resin containing 60% glass fiber. Added features of this grade include: Good Flow.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors
Building Component
Commercial Appliance
Home Appliances
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Auto Aftermarket

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	13	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	75	kJ/m²	ISO 180/1U
Multiaxial Impact	4	J	ISO 6603
Izod Impact, notched, 23°C	153	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1250	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	10	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	240	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	20570	MPa	ISO 527
Flexural Stress	357	MPa	ISO 178
Flexural Modulus, 2 mm/min	18120	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	241	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Modulus, 5 mm/min	21840	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	371	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	17900	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption (23°C / 50% RH)	0.73	%	ISO 62
Specific Gravity	1.7	-	ASTM D792
Density	1.72	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.48	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.9 - 2	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	250	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	237	°C	ISO 75/Af
HDT, 0.45 MPa, 3.2 mm, unannealed	253	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	240	°C	ASTM D648
CTE, -30°C to 30°C, flow	1.0E-06	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	1.90E-06	1/°C	ASTM D696

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience