LNP™ THERMOCOMP™ Compound SF008

LNP THERMOCOMP SF008 is a compound based on Nylon 12 resin containing 40% Glass Fiber.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 12 (Nylon 12)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Low Moisture Absorption
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood
Building Component
Commercial Appliance
Electronic Components
Home Appliances
Sport/Leisure

Applications

Possible usage of material

Air Conditioning
Amusement Machine
Building Accessory
Document Handling
Engine Component

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1441	J/m	ASTM D4812
Izod Impact, notched, 23°C	256	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	75	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	18	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	225 - 240	°C
Front - Zone 3 Temperature	225 - 240	°C
Middle - Zone 2 Temperature	220 - 230	°C
Rear - Zone 1 Temperature	215 - 225	°C
Mold Temperature	70 - 80	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	135	MPa	ASTM D638
Tensile Strain, break	10.5	%	ASTM D638
Tensile Modulus, 50 mm/min	8270	MPa	ASTM D638
Flexural Stress	96	MPa	ASTM D790
Flexural Modulus	7580	MPa	ASTM D790
Tensile Stress, break	152	MPa	ISO 527
Tensile Strain, break	9	%	ISO 527
Tensile Modulus, 1 mm/min	8760	MPa	ISO 527
Flexural Stress	213	MPa	ISO 178
Flexural Modulus	9000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.37	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.7	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.18	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.73	%	ISO 294
Density	1.37	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	176	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	170	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	166	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES