LNP™ THERMOCOMP™ Compound SF00A

LNP THERMOCOMP SF00A compound is based on Nylon 12 resin containing 50% glass fiber.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 12 (Nylon 12)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Battery Cell
Electronic Components
Personal Computing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	833	J/m	ASTM D4812
Izod Impact, notched, 23°C	160	J/m	ASTM D256
Multiaxial Impact	16	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	30	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	1	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	225 - 240	°C
Front - Zone 3 Temperature	225 - 240	°C
Middle - Zone 2 Temperature	220 - 230	°C
Rear - Zone 1 Temperature	215 - 225	°C
Mold Temperature	70 - 80	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	121	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	121	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	1.7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.7	%	ASTM D638
Tensile Modulus, 50 mm/min	12800	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	217	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	217	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	10984	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	113	MPa	ISO 527
Tensile Stress, break, 5 mm/min	113	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.5	%	ISO 527
Tensile Strain, break, 5 mm/min	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	12280	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.48	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.8 - 1	%	ASTM D955
Density	1.48	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	176	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	166	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES