LNP™ THERMOCOMP™ Compound TF002

LNP THERMOCOMP TF002 compound is based on Polyurethane (TPU) resin containing 10% glass fiber.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyurethane, Unspecified (PUR, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets
Sport/Leisure

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1230	J/m	ASTM D4812
Izod Impact, notched, 23°C	334	J/m	ASTM D256
Multiaxial Impact	24	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	29	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	129	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	31	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 105	°C
Drying Time	2	Hrs
Maximum Moisture Content	0.03	%
Melt Temperature	210	°C
Nozzle Temperature	205 - 225	°C
Front - Zone 3 Temperature	200 - 220	°C
Middle - Zone 2 Temperature	195 - 215	°C
Rear - Zone 1 Temperature	195 - 210	°C
Mold Temperature	15 - 45	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Shot to Cylinder Size	40 - 80	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	42	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	38	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	32.5	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	53	%	ASTM D638
Tensile Modulus, 50 mm/min	1460	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	900	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	43	MPa	ISO 527
Tensile Stress, break, 5 mm/min	40	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	33.6	%	ISO 527
Tensile Strain, break, 5 mm/min	55.4	%	ISO 527
Tensile Modulus, 1 mm/min	1260	MPa	ISO 527
Flexural Stress	26	MPa	ISO 178
Flexural Modulus, 2 mm/min	950	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.31	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.4	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.6 - 0.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D955
Density	1.31	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.61	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	152	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	67	°C	ASTM D648
CTE, -30°C to 30°C, flow	8.9E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	1.7E-04	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	148	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	61	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES