LNP™ THERMOCOMP™ Compound TF006H

LNP THERMOCOMP TF006H is a compound based on Polyurethane (TPU) containing 30% Glass Fiber. Added features include: Healthcare

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyurethane, Unspecified (PUR, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Healthcare/Formula lock
No PFAS intentionally added

Industry

Material previously used in

General Healthcare
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Surgical Devices
Healthcare

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1750	J/m	ASTM D4812
Izod Impact, notched, 23°C	512	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	19	J	ASTM D3763
Multiaxial Impact	17	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	131	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	41	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 105	°C
Drying Time	2	Hrs
Maximum Moisture Content	0.03	%
Melt Temperature	210	°C
Nozzle Temperature	205 - 225	°C
Front - Zone 3 Temperature	200 - 220	°C
Middle - Zone 2 Temperature	195 - 215	°C
Rear - Zone 1 Temperature	195 - 210	°C
Mold Temperature	15 - 45	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Shot to Cylinder Size	40 - 80	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	49	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	16.3	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	16	%	ASTM D638
Tensile Modulus, 50 mm/min	1480	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	58	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1690	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	51	MPa	ISO 527
Tensile Stress, break, 5 mm/min	51	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	15.5	%	ISO 527
Tensile Strain, break, 5 mm/min	16	%	ISO 527
Tensile Modulus, 1 mm/min	1800	MPa	ISO 527
Flexural Modulus, 2 mm/min	2180	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.47	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.36	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.8	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.15	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.4	%	ISO 294
Density	1.47	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.5	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	167	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	78	°C	ASTM D648
CTE, -40°C to 40°C, flow	2.7E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.3E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.84E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.31E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	167	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	85	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience