LNP THERMOCOMP UF004AS compound is based on Polyphthalamide (PPA) resin containing 20% glass fiber. Added features of this grade include: Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 315 - 330 | °C | |
| Front - Zone 3 Temperature | 325 - 340 | °C | |
| Middle - Zone 2 Temperature | 315 - 325 | °C | |
| Rear - Zone 1 Temperature | 310 - 320 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 136 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 178 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.4 | % | SABIC method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 256 | °C | ISO 75/Af |