LNP THERMOCOMP UF0067W compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Strength, in oil, 0.8 mm | 29.7 | kV/mm | ASTM D149 |
| Relative Permittivity, 1 kHz | 4.05 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 3.82 | - | ASTM D150 |
| Dissipation Factor, 1 kHz | 0.0115 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.0128 | - | ASTM D150 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 662 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Melt Temperature | 280 - 320 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Front - Zone 3 Temperature | 280 - 320 | °C | |
| Middle - Zone 2 Temperature | 280 - 320 | °C | |
| Rear - Zone 1 Temperature | 250 - 280 | °C | |
| Mold Temperature | 90 - 120 | °C | |
| Back Pressure | 1 - 5 | MPa | |
| Screw Speed | 30 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 143 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 10540 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 213 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 10200 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 128 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11310 | MPa | ISO 527 |
| Flexural Stress | 189 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9130 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 - 1.5 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 - 1.5 | % | ISO 294 |
| Density | 1.45 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 299 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 281 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.34E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.04E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.11E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 277 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |