LNP THERMOCOMP UF006H compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Healthcare.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 47 | kJ/m² | ISO 180/1U |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 683 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy @ peak, 23°C | 7 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 315 - 330 | °C | |
| Front - Zone 3 Temperature | 325 - 340 | °C | |
| Middle - Zone 2 Temperature | 315 - 325 | °C | |
| Rear - Zone 1 Temperature | 310 - 320 | °C | |
| Mold Temperature | 150 - 170 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 208 | MPa | ISO 527 |
| Tensile Stress, break | 208 | MPa | ISO 527 |
| Tensile Strain, yield | 2 | % | ISO 527 |
| Tensile Strain, break | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12440 | MPa | ISO 527 |
| Tensile Stress, yield | 224 | MPa | ASTM D638 |
| Flexural Stress | 294 | MPa | ISO 178 |
| Flexural Modulus | 11000 | MPa | ISO 178 |
| Tensile Stress, break | 224 | MPa | ASTM D638 |
| Tensile Strain, yield | 2.2 | % | ASTM D638 |
| Tensile Strain, break | 2.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 13100 | MPa | ASTM D638 |
| Flexural Stress | 289 | MPa | ASTM D790 |
| Flexural Modulus | 11030 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.37 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.77 | % | ISO 294 |
| Density | 1.53 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 293 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 282 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 2.80E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.10E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 305 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 287 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.88E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.04E-05 | 1/°C | ASTM E831 |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.