IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP UF008AS compound is based on Polyphthalamide (PPA) resin containing 40% glass fiber. Added features of this grade include: Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 | % | |
Melt Temperature | 315 - 330 | °C | |
Front - Zone 3 Temperature | 325 - 340 | °C | |
Middle - Zone 2 Temperature | 315 - 325 | °C | |
Rear - Zone 1 Temperature | 310 - 320 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 234 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 14500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 315 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 12000 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.14 | % | SABIC method |
Density | 1.53 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.3E-05 | 1/°C | ISO 11359-2 |