LNP THERMOCOMP UX06032 compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1E+15 - 1E+17 | Ω.cm | ASTM D257 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.41 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.41 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Yellow Card Link 2 | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.41 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 0.8 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.6 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 0.8 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.6 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Melt Temperature | 305 - 315 | °C | |
| Front - Zone 3 Temperature | 295 - 315 | °C | |
| Middle - Zone 2 Temperature | 290 - 310 | °C | |
| Rear - Zone 1 Temperature | 280 - 300 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 40 - 80 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11400 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9900 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.3 | % | SABIC method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.23 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 275 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 140 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.