LNP THERMOCOMP VF008A compound is based on super tough Nylon 66 resin containing 40% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1010 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 187 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 280 - 295 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 275 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 270 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 158 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 - 4 | % | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 227 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8270 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.41 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.6 | % | ASTM D570 |
| Mold Shrinkage, flow | 0.4 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 249 | °C | ASTM D648 |