LNP THERMOCOMP WC003 compound is based on Polybutylene Terephthalate (PBT) resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+04 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 240 - 265 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 220 - 230 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 136 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 193 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.4 | % | SABIC method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.16E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 224 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 206 | °C | ISO 75/Af |