LNP THERMOCOMP WF0069 compound is based on Polybutylene Terephthalate (PBT) resin containing 30% glass fiber. Added features of this grade include: Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 0.73 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 370 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 230 - 255 | °C | |
| Front - Zone 3 Temperature | 240 - 260 | °C | |
| Middle - Zone 2 Temperature | 235 - 250 | °C | |
| Rear - Zone 1 Temperature | 230 - 240 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 40 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Strength, 1.3 mm/min, 50 mm span | 165 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9650 | MPa | ASTM D790 |
| Tensile Stress, brk, Type I, 5 mm/min | 121 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.5 | % | ASTM D955 |
| Water Absorption, (23°C/24hrs) | 0.06 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 204 | °C | ASTM D648 |