LNP™ THERMOCOMP™ Compound WF006V

LNP THERMOCOMP WF006V compound is based on Polybutylene Terephthalate (PBT) containing 30% glass fiber. This material has fast plating capability and stable RF performance. Added features of this grade include wide processing window and chemical resistance. It makes a good candidate for internal and external parts of Laser Direct Structuring (LDS) applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Impact resistant
Laser Direct Structuring
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Mobile Phone - Computer - Tablets
Speaker - Earphone
Wireless Communication

Applications

Possible usage of material

Mobile Phone
Antenna
Sensor
Wearables
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.503	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0106	-	SABIC method
Dielectric Constant, 1.9 GHz	3.53	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0101	-	SABIC method
Dielectric Constant, 5 GHz	3.543	-	SABIC method
Dissipation Factor, 5 GHz	0.00923	-	SABIC method
Dielectric Constant, 10 GHz	3.54	-	SABIC method
Dissipation Factor, 10 GHz	0.00893	-	SABIC method
Dielectric Constant, 20 GHz	3.357	-	SABIC method
Dissipation Factor, 20 GHz	0.00869	-	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	116	J/m	ASTM D256
Izod Impact, unnotched, 23°C	695	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	10.56	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	38.32	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10.91	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	45.91	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	240 - 260	°C
Nozzle Temperature	240 - 260	°C
Front - Zone 3 Temperature	240 - 260	°C
Middle - Zone 2 Temperature	240 - 260	°C
Rear - Zone 1 Temperature	240 - 260	°C
Mold Temperature	110 - 130	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	90 - 110	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	94	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	2.5	%	ASTM D638
Tensile Modulus, 50 mm/min	8049	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	140	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7100	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	95	MPa	ISO 527
Tensile Strain, break, 50 mm/min	2.55	%	ISO 527
Tensile Modulus, 1 mm/min	8260	MPa	ISO 527
Flexural Strength, 2 mm/min	138	MPa	ISO 178
Flexural Modulus, 2 mm/min	6839	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.5	-	ASTM D792
Melt Volume Rate, MVR at 270°C/5 kg	12.3	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.30	%	SABIC method
Mold Shrinkage, xflow	0.47	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	205	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	158	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	204	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	153	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	2.13E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.31E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.10E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.74E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	149	°C	ISO 306
Vicat Softening Temp, Rate B/120	148	°C	ASTM D1525

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES