LNP THERMOCOMP WX15003 compound is based on Polybutylene Terephthalate (PBT) resin containing 45 % glass fiber/mineral. Added features of this grade include UV stabilized and high specific gravity.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Relative Permittivity, 1 MHz | 3.5 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.013 | - | IEC 60250 |
| Relative Permittivity, 50/60 Hz | 3.6 | - | IEC 60250 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 31 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255 - 280 | °C | |
| Nozzle Temperature | 245 - 270 | °C | |
| Front - Zone 3 Temperature | 250 - 270 | °C | |
| Middle - Zone 2 Temperature | 240 - 260 | °C | |
| Rear - Zone 1 Temperature | 230 - 250 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 60 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Taber Abrasion, CS-17, 1 kg | 76 | mg/1000cy | SABIC method |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 140 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7400 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 145 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.6 | % | SABIC method |
| Density | 1.83 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 11 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 0.33 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 180 | °C | ISO 75/Ae |