LNP THERMOCOMP WX88406 compound is based on Polybutylene Terephthalate (PBT) resin containing 25 % glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 681 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 240 - 265 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 220 - 230 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 103 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 103 | MPa | ASTM D638 |
| Tensile Strain, break | 2.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 7920 | MPa | ASTM D638 |
| Flexural Stress | 165 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 165 | MPa | ASTM D790 |
| Flexural Modulus | 7060 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7060 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 202 | °C | ASTM D648 |