IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 117.5 | J/m | ASTM D256 |
LNP THERMOCOMP WX96784 compound is based on Polybutylene Terephthalate (PBT) resin containing 25% mineral. Added features of this grade include: Improved CTI, Flame Retardant, Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 117.5 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Melt Temperature | 248 - 276 | °C | |
Mold Temperature | 80 - 93 | °C | |
Screw Speed | 40 - 80 | rpm | |
Back Pressure | .334 | MPa |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 52 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 10 - 15 | % | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3103 | MPa | ASTM D790 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 97 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Water Absorption, (23°C/24hrs) | .05 | % | ASTM D570 |
Specific Gravity | 1.5 | - | ASTM D792 |
Mold Shrinkage, 48 hrs @ 23°C, flow | 1.10 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 77 | °C | ASTM D648 |