LNP THERMOCOMP YF005 compound is based on Thermoplastic Polyester Elastomer (TPE) resin containing 25% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 998 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 331 | J/m | ASTM D256 |
| Multiaxial Impact | 7 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 76 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 215 - 240 | °C | |
| Front - Zone 3 Temperature | 225 - 240 | °C | |
| Middle - Zone 2 Temperature | 205 - 215 | °C | |
| Rear - Zone 1 Temperature | 180 - 195 | °C | |
| Mold Temperature | 25 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 47 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 46 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 9.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 8.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2370 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1980 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 46 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 9.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 10.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2360 | MPa | ISO 527 |
| Flexural Stress | 53 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2120 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.4 | - | ASTM D792 |
| Density | 1.4 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.31 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.41 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 186 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 152 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 3.6E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 1.77E-04 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1250 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 331 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 54 | MPa | ASTM D638 |
| Tensile Strain, break | 8.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2730 | MPa | ASTM D638 |
| Flexural Stress | 68 | MPa | ASTM D790 |
| Flexural modulus | 2530 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.4 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 170 | °C | ASTM D648 |