LNP THERMOCOMP ZKC08 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 40% minerals and impact modifier. Added features of this grade include: High Dielectric Constant (Dk), Extremely Low Dissipation Factor (Df), Good Ductility and Good Thermal Performance,High Impact Resistance.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.91 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.0009 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.93 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.0012 | - | SABIC method |
| Dielectric Constant, 5 GHz | 3.95 | - | SABIC method |
| Dissipation Factor, 5 GHz | 0.0018 | - | SABIC method |
| Dielectric Constant, 10 GHz | 3.93 | - | SABIC method |
| Dissipation Factor, 10 GHz | 0.0021 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 205 | J/m | ASTM D256 |
| Izod Impact, notched, -20°C | 166 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 21 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 16 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Melt Temperature | 285 - 320 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Front - Zone 3 Temperature | 285 - 320 | °C | |
| Middle - Zone 2 Temperature | 280 - 310 | °C | |
| Rear - Zone 1 Temperature | 275 - 300 | °C | |
| Mold Temperature | 90 - 120 | °C | |
| Back Pressure | 0.3 - 0.9 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 65 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 63 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2000 | MPa | ASTM D790 |
| Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 36 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7.8 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 8.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2170 | MPa | ASTM D638 |
| Flexural Stress, yield, 2 mm/min | 72 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2230 | MPa | ISO 178 |
| Tensile Stress, break, 50 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 9.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2080 | MPa | ISO 527 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melt Volume Rate, MVR at 300°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 300°C/10.0 kg | 23.5 | cm³/10 min | ISO 1133 |
| Melt Flow Rate, 300°C/5.0 kgf | 9.5 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 300°C/10 kgf | 31 | g/10 min | ASTM D1238 |
| Mold Shrinkage, flow, 24 hrs | 0.75 - 0.85 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.75 - 0.85 | % | ASTM D955 |
| Water Absorption, (23°C/24hrs) | 0.03 | % | ISO 62-1 |
| Density | 1.43 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 148 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 173 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 174 | °C | ISO 75/Bf |
| CTE, -40°C to 150°C, flow | 6.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 150°C, xflow | 8.3E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |