LNP™ THERMOCOMP™ Compound ZKC0CV

LNP THERMOCOMP ZKC0CV compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing proprietary fillers. Added features of this grade include: High Dielectric Constant (Dk), Low Dissipation Factor (Df) for Laser Direct Structuring (LDS) and Good Thermal Performance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
Dimensional stability
Heat Stabilized
Laser Direct Structuring
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Mobile Phone - Computer - Tablets
Speaker - Earphone
Wireless Communication

Applications

Possible usage of material

Automotive
Mobile Phone
Antenna
Electronic Components
Electronics
Infrastructure
Wearables
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	6.8	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0013	-	SABIC method
Dielectric Constant, 1.9 GHz	6.8	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0013	-	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	50.6	J/m	ASTM D256
Izod Impact, notched, -30°C	25	J/m	ASTM D256
Izod Impact, unnotched, 23°C	266	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	5.3	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	3.8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	19	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	4.5	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	2.3	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	23	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	105 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	290 - 325	°C
Nozzle Temperature	290 - 325	°C
Front - Zone 3 Temperature	290 - 325	°C
Middle - Zone 2 Temperature	280 - 320	°C
Rear - Zone 1 Temperature	270 - 310	°C
Mold Temperature	90 - 120	°C
Back Pressure	0.3 - 0.9	MPa
Screw Speed	50 - 150	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	62	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.7	%	ASTM D638
Tensile Modulus, 5 mm/min	5880	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	90	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	5200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	61	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.6	%	ISO 527
Tensile Modulus, 1 mm/min	5780	MPa	ISO 527
Flexural Strength, 2 mm/min	95	MPa	ISO 178
Flexural Modulus, 2 mm/min	5820	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	2	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.07	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.02	%	ISO 62-4
Melt Volume Rate, MVR at 300°C/5.0 kg	5.2	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.6 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.7 - 0.9	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	143	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	134	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	145	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	136	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	5.2E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	5.4E-5	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES