LNP THERMOCOMP ZX08005 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing unreinforced. Added features of this grade include: Improved Dielectric Properties.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Relative Permittivity, 100 MHz | 6.58 | - | IEC 60250 |
| Relative Permittivity, 500 MHz | 6.47 | - | IEC 60250 |
| Relative Permittivity, 1 GHz | 6.16 | - | IEC 60250 |
| Dissipation Factor, 500 MHz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 GHz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 MHz | 0.001 | - | IEC 60250 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 300 - 305 | °C | |
| Front - Zone 3 Temperature | 300 - 310 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 275 - 290 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 2.07 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 140 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 130 | °C | ASTM D648 |