LNP™ THERMOCOMP™ Compound ZX08309

LNP THERMOCOMP ZX08309 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing proprietary fillers. Added features of this grade include: High Dielectric Constant and Low Loss Tangent.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Cooking Range
Wireless Communications
Wiring Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant (Dk), 1.1 GHz	4.4 - 4.6	-	ASTM ES 7-83
Dissipation Factor (Df), 1.1 GHz	0.002 - 0.004	-	ASTM ES 7-83

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	60	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	105	°C
Drying Time	3 - 5	Hrs
Melt Temperature	295 - 305	°C
Nozzle Temperature	290 - 295	°C
Front - Zone 3 Temperature	300 - 305	°C
Middle - Zone 2 Temperature	290 - 295	°C
Rear - Zone 1 Temperature	280 - 285	°C
Mold Temperature	90	°C
Back Pressure	9	MPa
Screw Speed	100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Flexural Stress, brk, 1.3 mm/min, 50 mm span	90 - 100	MPa	ASTM D790
Flexural Modulus, 2 mm/min	3200 - 3500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 24 hrs	0.7	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.65	%	ASTM D955
Density	1.66	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/5.0 kg	11	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	134	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	122	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES