THERMOTUF AX06401 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 20% glass fiber. Added features of this grade include: Improved Toughness.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 39 | kJ/m² | ISO 180/1U |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 450 | J/m | ASTM D4812 |
| Instrumented Dart Impact Total Energy, 23°C | 11 | J | ASTM D3763 |
| Instrumented Dart Impact Energy @ peak, 23°C | 10 | J | ASTM D3763 |
| Instrumented Dart Impact Peak Force, 23°C | 626 | N | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 70 - 90 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 250 - 270 | °C | |
| Rear - Zone 1 Temperature | 205 - 215 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | - | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 7000 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 6600 | MPa | ISO 178 |
| Flexural Strength, 2 mm/min | 146 | MPa | ISO 178 |
| Tensile Stress, brk, Type I, 5 mm/min | 93 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 6800 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5650 | MPa | ASTM D790 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 141 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.04 | % | ISO 62-4 |
| Mold Shrinkage, flow | 1.64 | % | SABIC method |
| Mold Shrinkage, xflow | 1.73 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| Vicat Softening Temp, Rate A/50 | 117 | °C | ASTM D1525 |
| CTE, -40°C to 40°C, flow | 3.93E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.07E-05 | 1/°C | ASTM E831 |
| Vicat Softening Temp, Rate A/50 | 117 | °C | ISO 306 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 102 | °C | ASTM D648 |