LNP™ THERMOTUF™ Compound DF004PSI

LNP THERMOTUF DF004PSI compound is based on Polycarbonate (PC) resin containing 20% glass fiber. Added features of this grade include: Impact Modified, High Flow Ductile, Good Chemical Resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
High Flow
High stiffness/Strength
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	0.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Charpy Impact, unnotched, 23°C	48	kJ/m²	ISO 179/2C
Izod Impact, unnotched, 23°C	627	J/m	ASTM D4812
Izod Impact, notched, 23°C	160	J/m	ASTM D256
Charpy Impact, notched, 23°C	16	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Nozzle Temperature	285 - 305	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	99	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.9	%	ASTM D638
Tensile Modulus, 5 mm/min	6100	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	147	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	5380	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	99	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.9	%	ISO 527
Tensile Modulus, 1 mm/min	5960	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.33	g/cm³	ASTM D792
Mold Shrinkage, flow	0.3 - 0.5	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	10	cm³/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	130	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	126	°C	ASTM D648
CTE, -40°C to 40°C, flow	2.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards