LNP THERMOTUF OF006IXQ compound is based on linear Polyphenylene Sulfide (PPS) resin containing 30% glass fiber. Added features include: Impact Modified, High Heat Resistance and Chemical Resistance.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-1 Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | ≥3.0 | mm | UL 94 |
| UV-light, water exposure/immersion | f1 | - | UL 746C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 156 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 820 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Hopper Temperature | 50 - 70 | °C | |
| Melt Temperature | 310 - 330 | °C | |
| Front - Zone 3 Temperature | 310 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 330 | °C | |
| Rear - Zone 1 Temperature | 290 - 320 | °C | |
| Mold Temperature | 130 - 160 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 150 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 10000 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 220 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9400 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 150 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10100 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 220 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melt Flow Rate, 315°C/5.0 kgf | 21 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 315°C/5.0 kg | 14 | cm³/10 min | ISO 1133 |
| Specific Gravity | 1.51 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.02 | % | ISO 62-4 |
| Moisture Absorption, (23°C/50% RH/Equilibrium) | 0.02 | % | ISO 62-4 |
| Water Absorption, (23°C/24hrs) | 0.05 | % | ISO 62-1 |
| Mold Shrinkage, flow | 0.2 | % | SABIC method |
| Mold Shrinkage, xflow | 0.6 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 275 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 260 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 278 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Af |
| CTE, -40°C to 90°C, flow | 1.3E-5 | 1/°C | ASTM E831 |
| CTE, -40°C to 90°C, xflow | 5.3E-5 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.2E-5 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.7E-5 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 90°C, flow | 1.3E-5 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 90°C, xflow | 5.2E-5 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |