FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
LNP THERMOTUF OF008I compound is based on linear Polyphenylene Sulfide (PPS) resin containing 40% glass fiber. Added features of this grade include: Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Front - Zone 3 Temperature | 330 - 345 | °C | |
Middle - Zone 2 Temperature | 320 - 330 | °C | |
Rear - Zone 1 Temperature | 305 - 315 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 129 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 11800 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 193 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 11000 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.56 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.3E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.4E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 275 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 235 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |