LNP THEMROTUF PF003IU compound is based on Nylon 6 resin containing 15% glass fiber. Added features of this grade include: Impact Modified and UV Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 65 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 610 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3 | Hrs | |
| Maximum Moisture Content | .02 | % | |
| Melt Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 245 - 260 | °C | |
| Front - Zone 3 Temperature | 250 - 265 | °C | |
| Middle - Zone 2 Temperature | 245 - 260 | °C | |
| Rear - Zone 1 Temperature | 240 - 255 | °C | |
| Mold Temperature | 65 - 90 | °C | |
| Screw Speed | 50 - 80 | rpm | |
| Back Pressure | 0.3 - 0.7 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4100 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D790 |
| Tensile Stress, brk, Type I, 50 mm/min | 103 | MPa | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 197 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 201 | °C | ASTM D1525 |