LNP THERMOTUF PF006I compound is based on Nylon 6 resin containing 30% glass fiber. Added features of this grade include: Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 727 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 16 | J | ASTM D3763 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 50 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 97 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 8.1 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8500 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 157 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6820 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 35 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 99 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 9650 | MPa | ISO 527 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.35 | - | ASTM D792 |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.83 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.9 - 2 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.11 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.62 - 0.67 | % | ISO 294 |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.83 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 70 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B |