LNP THERMOTUF V1000 compound is based on unfilled Super Tough Nylon resin. Added features of this grade include: Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Instrumented Dart Impact Energy @ peak, 23°C | 56 | J | ASTM D3763 |
| Multiaxial Impact | 77 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 84 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 270 - 295 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 270 - 280 | °C | |
| Rear - Zone 1 Temperature | 260 - 270 | °C | |
| Mold Temperature | 50 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 10 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 45 | MPa | ASTM D638 |
| Tensile Stress, break | 50 | MPa | ASTM D638 |
| Tensile Strain, yield | 4.6 | % | ASTM D638 |
| Tensile Strain, break | 60.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 1930 | MPa | ASTM D638 |
| Flexural Stress | 74 | MPa | ASTM D790 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Tensile Stress, yield | 44 | MPa | ISO 527 |
| Tensile Stress, break | 50 | MPa | ISO 527 |
| Tensile Strain, yield | 17.1 | % | ISO 527 |
| Tensile Strain, break | 168.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1800 | MPa | ISO 527 |
| Flexural Stress | 64 | MPa | ISO 178 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.073 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.8 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1.3 - 1.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.3 - 1.5 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 1.3 - 1.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.3 - 1.5 | % | ISO 294 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.37 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 53 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.27E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.26E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.27E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.26E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 56 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.