LNP™ THERMOTUF™ Compound V1000UXC

LNP THERMOTUF V1000UXC compound is based on Super Tough Nylon resin. Added features of this grade include: Impact Modified, UV Stabilized.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
No PFAS intentionally added
Weatherable/UV stable

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Enclosure/Housing/Cover
Enclosures

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Multiaxial Impact	49	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	49	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	270 - 295	°C
Front - Zone 3 Temperature	290 - 300	°C
Middle - Zone 2 Temperature	270 - 280	°C
Rear - Zone 1 Temperature	260 - 270	°C
Mold Temperature	50 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	10 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	39	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	39	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	57.2	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	84.5	%	ASTM D638
Tensile Modulus, 5 mm/min	1710	MPa	ASTM D638
Flexural Stress	55	MPa	ASTM D790
Flexural Modulus	2060	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	41	MPa	ISO 527
Tensile Stress, break, 5 mm/min	41	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	146.7	%	ISO 527
Tensile Strain, break, 5 mm/min	165	%	ISO 527
Tensile Modulus, 1 mm/min	1650	MPa	ISO 527
Flexural Stress	53	MPa	ISO 178
Flexural Modulus	1700	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.07	-	ASTM D792
Density	1.065	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.6	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	2.1 - 2.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	2.5 - 2.7	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	2.2	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	2.6	%	ISO 294
Density	1.08	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	1	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	192	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	193	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.35E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.33E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.34E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.34E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	150	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	147	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas