LNP THERMOTUF VF003 compound is based on Super Touch Nylon resin containing 15% glass fiber. Added features of this grade include: Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 608 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 280 - 295 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 275 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 270 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 77 | MPa | ASTM D638 |
| Tensile Strain, break | 2.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 5010 | MPa | ASTM D638 |
| Flexural Stress | 124 | MPa | ASTM D790 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 241 | °C | ASTM D648 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |