LNP THERMOTUF VX99809 compound is based on Super Tough Nylon resin containing proprietary fillers. Added features of this grade include: Impact Modified, Easy Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1330 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 885 | J/m | ASTM D256 |
| Multiaxial Impact | 49 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 145 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 82 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 280 - 295 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 275 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 270 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 43 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 40 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 75.4 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 1980 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1220 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 42 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 41 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 129 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1880 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 1300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.084 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.92 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 2 - 3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2 - 3 | % | ASTM D955 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.9 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 178 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 49 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 100 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 47 | °C | ISO 75/Af |