LNP THERMOTUF WF008N compound is based on Polybutylene Terephthalate (PBT) resin containing 40% glass fiber. Added features of this grade include: Impact Modified, Good Metal Bonding Strength and Good Chemical Resistance targeted for Nano-Molding Technology (NMT) applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.78 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.76 | - | SABIC method |
| Dielectric Constant, 5 GHz | 3.73 | - | SABIC method |
| Dielectric Constant, 10 GHz | 3.80 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.0104 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.0096 | - | SABIC method |
| Dissipation Factor, 5 GHz | 0.0091 | - | SABIC method |
| Dissipation Factor, 10 GHz | 0.0082 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 960 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 145 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 106 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 59 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 11 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 275 | °C | |
| Front - Zone 3 Temperature | 250 - 270 | °C | |
| Middle - Zone 2 Temperature | 250 - 270 | °C | |
| Rear - Zone 1 Temperature | 240 - 260 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 100 - 160 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 133 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 11600 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 205 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11000 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 134 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11700 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 217 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 11200 | MPa | ISO 178 |
| Bonding Strength ("T" treatment, shear type) | 34 | MPa | ISO 19095 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 250°C/5.0 kgf | 10 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 275°C/5 kgf | 22 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 275°C/5 kg | 15 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.25 | % | SABIC method |
| Mold Shrinkage, xflow | 0.65 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 193 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 217 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 196 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Bf |
| CTE, -40°C to 40°C, flow | 1.9E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.7E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 50°C, flow | 1.7E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 50°C, xflow | 9.0E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 50°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 50°C, xflow | 8.9E-05 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature