LNP™ THERMOTUF™ Compound WF008NAQ

LNP THERMOTUF WF008NAQ (experimental grade name as ER008997) is a PBT/glass fiber compound for nano-molding technology (NMT) application. Added features of this material include: high modulus, low dielectric constant (Dk), high metal bonding force, good impact, and good color stability during anodizing.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
High stiffness/Strength
Impact resistant
Nano molding technology
No PFAS intentionally added

Industry

Material previously used in

Personal Accessory

Applications

Possible usage of material

Displays
Electrical Components & Infrastructure
Electrical

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.3	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0077	-	SABIC method
Dielectric Constant, 1.9 GHz	3.31	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0076	-	SABIC method
Dielectric Constant, 5 GHz	3.35	-	SABIC method
Dissipation Factor, 5 GHz	0.0072	-	SABIC method
Dielectric Constant, 10 GHz	3.35	-	SABIC method
Dissipation Factor, 10 GHz	0.0069	-	SABIC method
Dielectric Constant, 20 GHz	3.32	-	SABIC method
Dissipation Factor, 20 GHz	0.0071	-	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	150	J/m	ASTM D256
Izod Impact, notched, -30°C	130	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1000	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	14.7	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	13.3	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	55	kJ/m²	ISO 180/1U
Charpy Impact, notched, 23°C	15.5	kJ/m²	ISO 179/2C
Charpy Impact, notched, -30°C	14.3	kJ/m²	ISO 179/2C
Charpy Impact, unnotched, 23°C	60	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Hopper Temperature	40 - 60	°C
Melt Temperature	250 - 280	°C
Nozzle Temperature	255 - 280	°C
Front - Zone 3 Temperature	250 - 280	°C
Middle - Zone 2 Temperature	250 - 280	°C
Rear - Zone 1 Temperature	240 - 270	°C
Mold Temperature	100 - 160	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	133	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D638
Tensile Modulus, 5 mm/min	10100	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	201	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	9500	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	135	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.8	%	ISO 527
Tensile Modulus, 1 mm/min	10100	MPa	ISO 527
Flexural Strength, 2 mm/min	206	MPa	ISO 178
Flexural Modulus, 2 mm/min	9500	MPa	ISO 178
Bonding Strength ("T" treatment, shear type)	32	MPa	ISO 19095

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.51	g/cm³	ISO 1183
Melt Flow Rate, 275°C/5 kgf	15	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 275°C/5 kg	12	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.04	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.02	%	ISO 62-4
Mold Shrinkage, flow	0.2	%	SABIC method
Mold Shrinkage, xflow	0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	222	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	205	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	222	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Af
CTE
– -40°C to 40°C, flow	2.2E-05	1/°C	ASTM E831
– -40°C to 40°C, xflow	8.3E-05	1/°C	ASTM E831
– 50°C to 120°C, flow	1.3E-05	1/°C	ASTM E831
– 50°C to 120°C, xflow	1.6E-04	1/°C	ASTM E831
– -40°C to 40°C, flow	2.0E-05	1/°C	ISO 11359-2
– -40°C to 40°C, xflow	8.5E-05	1/°C	ISO 11359-2
– 50°C to 120°C, flow	1.1E-05	1/°C	ISO 11359-2
– 50°C to 120°C, xflow	1.9E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	201	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	198	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	201	°C	ISO 306
Vicat Softening Temp, Rate B/120	199	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES