LNP THERMOTUF WF009N compound is based on Polybutylene Terephthalate (PBT) resin containing 45% glass fiber. Added features of this grade include: Impact Modified, Good Metal Bonding Strength and Good Chemical Resistance targeted for Nano-Molding Technology (NMT) applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.94 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.95 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.011 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.010 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1050 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 153 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 144 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 64 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 16 | kJ/m² | ISO 180/1A |
| Charpy Impact, unnotched, 23°C | 72 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, 23°C | 17 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 16 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 4 - 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 265 - 285 | °C | |
| Nozzle Temperature | 265 - 285 | °C | |
| Front - Zone 3 Temperature | 265 - 285 | °C | |
| Middle - Zone 2 Temperature | 260 - 280 | °C | |
| Rear - Zone 1 Temperature | 250 - 270 | °C | |
| Mold Temperature | 100 - 140 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 168 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 14500 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 256 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13200 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 163 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14100 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 259 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12300 | MPa | ISO 178 |
| Bonding strength (TRI) , 5 mm/min, Type A | 40 | MPa | ISO 19095 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.7 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow | 0.14 | % | SABIC method |
| Mold Shrinkage, xflow | 0.34 | % | SABIC method |
| Melt Volume Rate, MVR at 275°C/5 kg | 29 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 212 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 215 | °C | ASTM D648 |
| Vicat Softening Temp, Rate A/50 | 213 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 211 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 1.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.6E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |