LNP THERMOTUF WF009NAR compound is based on Polybutylene Terephthalate (PBT) resin containing 45% glass fiber. Added features of this grade include: Impact Modified, Good Metal Bonding Strength and Good Chemical Resistance targeted for Nano-Molding Technology (NMT) applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.93 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.92 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.00792 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.00769 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 980 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 123 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 115 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 60 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact, unnotched, 23°C | 69 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 11 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 4 - 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 265 - 285 | °C | |
| Nozzle Temperature | 265 - 285 | °C | |
| Front - Zone 3 Temperature | 265 - 285 | °C | |
| Middle - Zone 2 Temperature | 260 - 280 | °C | |
| Rear - Zone 1 Temperature | 250 - 270 | °C | |
| Mold Temperature | 120 - 160 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 162 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 14900 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 242 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 237 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13700 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 172 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15700 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 264 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 13000 | MPa | ISO 178 |
| Bonding strength (TRI) , 5 mm/min, Type A | 42 | MPa | ISO 19095 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.7 | g/cm³ | ASTM D792 |
| Melt Volume Rate, MVR at 275°C/5 kg | 17 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 285°C/5.0 kg | 27 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 216 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 208 | °C | ASTM D648 |
| Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 1.7E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |