FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
LNP VERTON MV006S is a compound based on Polypropylene (PP) resin containing 30% long glass fiber. Added features include Chemically Coupled, Structural and Heat Stabilized.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 24 | kJ/m² | ISO 180/1A |
Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 24 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
Izod Impact, notched, 23°C | 195 | J/m | ASTM D256 |
Izod Impact, unnotched, 23°C | 460 | J/m | ASTM D4812 |
Multiaxial Impact | 14 | J | ISO 6603 |
Instrumented Dart Impact Energy @ peak, 23°C | 8 | J | ASTM D3763 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 220 - 250 | °C | |
Front - Zone 3 Temperature | 250 - 260 | °C | |
Middle - Zone 2 Temperature | 245 - 255 | °C | |
Rear - Zone 1 Temperature | 230 - 245 | °C | |
Mold Temperature | 40 - 65 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 110 | MPa | ISO 527 |
Tensile Strain, break | 2.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
Flexural Modulus | 6000 | MPa | ISO 178 |
Flexural Stress, yield, 2 mm/min | 135 | MPa | ISO 178 |
Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 |
Tensile Modulus, 5 mm/min | 7100 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 2.8 | % | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6100 | MPa | ASTM D790 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 135 | MPa | ASTM D790 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 130 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.12 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.008 | % | ISO 62 |
Water Absorption, (23°C/saturated) | 0.07 | % | ISO 62-1 |
Mold Shrinkage, flow, 24 hrs | 0.21 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.28 | % | ISO 294 |
Density | 1.12 | g/cm³ | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.03 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.21 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.28 | % | ASTM D955 |
Wear Factor Washer | 44 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.36 | - | ASTM D3702 Modified: Manual |
Static COF | 0.39 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 157 | °C | ISO 75/Af |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 164 | °C | ISO 75/Bf |
CTE, -40°C to 40°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.0E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 140 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 3.9E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.1E-05 | 1/°C | ASTM E831 |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |