LNP VERTON MV008SU is a compound based on Polypropylene (PP) resin containing 40% long glass fiber. Added features include Chemically Coupled, Structural, UV and Heat Stabilized.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 208 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 10 | J | ASTM D3763 |
| Multiaxial Impact | 10 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 220 - 250 | °C | |
| Front - Zone 3 Temperature | 250 - 260 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 245 | °C | |
| Mold Temperature | 40 - 65 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 119 | MPa | ASTM D638 |
| Tensile Strain, break | 2.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 9550 | MPa | ASTM D638 |
| Flexural Stress | 179 | MPa | ASTM D790 |
| Flexural Modulus | 7800 | MPa | ASTM D790 |
| Tensile Stress, break | 127 | MPa | ISO 527 |
| Tensile Strain, break | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10120 | MPa | ISO 527 |
| Flexural Stress | 187 | MPa | ISO 178 |
| Flexural Modulus | 8250 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.08 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.32 | % | ISO 294 |
| Density | 1.22 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 157 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 4.6E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.26E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 4.61E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.27E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 164 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 160 | °C | ISO 75/Af |