LNP VERTON MV00CS is a compound based on Polypropylene (PP) resin containing 60% long glass fiber. Added features include Chemically Coupled, Heat Stabilized and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 39 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 29 | kJ/m² | ISO 179/1eU |
| Izod Impact, notched, 23°C | 155 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 620 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 220 - 250 | °C | |
| Front - Zone 3 Temperature | 250 - 260 | °C | |
| Middle - Zone 2 Temperature | 245 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 245 | °C | |
| Mold Temperature | 40 - 65 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15100 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 13700 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 |
| Tensile Modulus, 5 mm/min | 17300 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.1 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13800 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 135 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.04 | % | ISO 62 |
| Mold Shrinkage, flow, 24 hrs | 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 154 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 160 | °C | ISO 75/Bf |
| HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |