LNP™ VERTON™ Compound MVL36SX0

LNP VERTON MVL36SX0 is a compound based on Polypropylene (PP) resin containing 30% long glass fiber and PTFE. Added features include Chemically coupled, Heat Stabilized, Wear Resistant and Structural.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Heat Stabilized
High stiffness/Strength
Wear resistant
Weatherable/UV stable

Industry

Material previously used in

Automotive Exteriors
Commercial Appliance
Home Appliances
Industrial General
Sport/Leisure
Water Management

Applications

Possible usage of material

Auto Aftermarket

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Multiaxial Impact	5	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	42	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	17	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	215 - 220	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	200 - 210	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	116	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	8500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	133	MPa	ISO 178
Flexural Modulus, 2 mm/min	6500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 24 hrs	0.37	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.73	%	ISO 294
Density	1.28	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.01	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	163	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	157	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES