LNP VERTON PVN1AESP is a compound based on Polyamide 6 (Nylon 6) resin containing 50% long glass fiber and proprietary lubricant. Added features include Easy Molding, Wear Resistant and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1300 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 250 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 80 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 90 | kJ/m² | ISO 179/1eU |
| Multiaxial Impact | 12 | J | ISO 6603 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Nozzle Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 0.05 - 0.15 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 220 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 16000 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 320 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 12000 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 220 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 16000 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 320 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.20 - 0.35 | % | ISO 294 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Af |