LNP VERTON PX06419 is a compound based on Polyamide 6 (Nylon 6) resin containing 50% long glass fiber and proprietary fillers. Added features include Heat Stabilized and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 357 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 228 | MPa | ASTM D638 |
| Tensile Strain, break | 2.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 17440 | MPa | ASTM D638 |
| Flexural Stress | 296 | MPa | ASTM D790 |
| Flexural Modulus | 15230 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |