IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 68 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
LNP VERTON PX91200 is a compound based on Polyamide 6 (Nylon 6) resin containing 35% long glass fiber and proprietary lubricants. Added features include High Impact, Structural and Wear resistant.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 68 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 265 - 275 | °C | |
Front - Zone 3 Temperature | 275 - 290 | °C | |
Middle - Zone 2 Temperature | 265 - 275 | °C | |
Rear - Zone 1 Temperature | 250 - 260 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 181 | MPa | ISO 527 |
Tensile Strain, break | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 12100 | MPa | ISO 527 |
Flexural Stress | 250 | MPa | ISO 178 |
Flexural Modulus | 10290 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.49 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 222 | °C | ISO 75/Af |