LNP VERTON RV0079SS is a compound based on Polyamide 66 (Nylon 66) resin containing 35% long glass fiber. Added features include Flame Retardant, Heat Stabilized and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥1.7 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 290 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 280 - 295 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 213 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 213 | MPa | ISO 527 |
| Tensile Strain, break | 1.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15070 | MPa | ISO 527 |
| Flexural Stress | 298 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min | 298 | MPa | ISO 178 |
| Flexural Modulus | 13280 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 13280 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 262 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 259 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |